Compare / 1.4301 vs 1.4307

1.4301 vs 1.4307

EN 10088-2/-3/-4/-5 · Stainless steel

The everyday austenitic stainless (304): fy 210 MPa plate, 230 MPa cold rolled strip.

EN 10088-2/-3/-4/-5 · Stainless steel

Low-carbon 304L: slightly lower strength than 1.4301, better after welding.

Mechanical

Property	Condition	1.4301	1.4307	Difference
0.2 % proof strength Rp0.2	t = 8 mm · cold rolled strip	≥ 230MPa1	≥ 220MPa1	−4.3 %
	t = 13.5 mm · hot rolled strip	≥ 210MPa1	≥ 200MPa1	−4.8 %
	t = 75 mm · hot rolled plate	≥ 210MPa2	≥ 200MPa2	−4.8 %
	t = 250 mm · bars, rods and sections	≥ 190MPa1	≥ 175MPa1	−7.9 %
Tensile strength Rm	t = 8 mm · cold rolled strip	≥ 540MPa1	≥ 520MPa1	−3.7 %
	t = 13.5 mm · hot rolled strip	≥ 520MPa1	≥ 520MPa1	same
	t = 75 mm · hot rolled plate	≥ 520MPa2	≥ 500MPa2	−3.8 %
	t = 250 mm · bars, rods and sections	≥ 500MPa1	≥ 500MPa1	same
Elongation after fracture A	t = 75 mm · hot rolled plate	≥ 45%1	≥ 45%1	same
Modulus of elasticity E	—	200 000MPa1	200 000MPa1	same
Shear modulus G	—	76 900MPa1	76 900MPa1	same
Poisson's ratio ν	—	0.31	0.31	same

Design values

Property	Condition	1.4301	1.4307	Difference
Partial factor for the material γM	cross-sections, γM0	1.11	1.11	same
	member instability, γM1	1.11	1.11	same
	tension to fracture, bolts, welds, γM2	1.251	1.251	same

Physical

Property	Condition	1.4301	1.4307	Difference
Density ρ	—	7 900kg/m³1	7 900kg/m³1	same

Thermal

Property	Condition	1.4301	1.4307	Difference
Coefficient of thermal expansion α	20–100 °C	16×10⁻⁶ /K1	16×10⁻⁶ /K1	same
Specific heat capacity cp	at +20 °C	500J/(kg·K)1	500J/(kg·K)1	same
Thermal conductivity λ	at +20 °C	15W/(m·K)1	15W/(m·K)1	same

Chemical and durability

Property	Condition	1.4301	1.4307	Difference
Corrosion resistance class CRC	—	II1	II1

Fire

Property	Condition	1.4301	1.4307	Difference
0.2 % proof strength reduction factor in fire kp0.2,θ	at +20 °C	11	11	same
	at +100 °C	0.781	0.781	same
	at +200 °C	0.651	0.651	same
	at +300 °C	0.61	0.61	same
	at +400 °C	0.551	0.551	same
	at +500 °C	0.51	0.51	same
	at +600 °C	0.461	0.461	same
	at +700 °C	0.381	0.381	same
	at +800 °C	0.251	0.251	same
	at +900 °C	0.151	0.151	same
	at +1000 °C	0.071	0.071	same
	at +1100 °C	0.051	0.051	same
Elastic modulus reduction factor kE,θ	at +20 °C	11	11	same
	at +100 °C	0.961	0.961	same
	at +200 °C	0.921	0.921	same
	at +300 °C	0.881	0.881	same
	at +400 °C	0.841	0.841	same
	at +500 °C	0.81	0.81	same
	at +600 °C	0.761	0.761	same
	at +700 °C	0.711	0.711	same
	at +800 °C	0.631	0.631	same
	at +900 °C	0.451	0.451	same
	at +1000 °C	0.21	0.21	same
	at +1100 °C	0.11	0.11	same
Ultimate strength reduction factor ku,θ	at +20 °C	11	11	same
	at +100 °C	0.811	0.811	same
	at +200 °C	0.721	0.721	same
	at +300 °C	0.681	0.681	same
	at +400 °C	0.661	0.661	same
	at +500 °C	0.611	0.611	same
	at +600 °C	0.541	0.541	same
	at +700 °C	0.41	0.41	same
	at +800 °C	0.251	0.251	same
	at +900 °C	0.131	0.131	same
	at +1000 °C	0.081	0.081	same
	at +1100 °C	0.051	0.051	same

Rows are matched by condition (thickness band, temperature, product form). A dash means the grade has no sourced value for that condition. Differences are 1.4307 relative to 1.4301; for ranges the lower bound is compared.