Compare / SD390 vs SD490
SD390 vs SD490
JIS G 3112 · Steel
Japanese deformed bar: yield 390–510 MPa, tensile ≥ 560 MPa, yield ratio ≤ 80 %.
JIS G 3112 · Steel
Japanese deformed bar: yield 490–625 MPa, tensile ≥ 620 MPa, yield ratio ≤ 80 %.
Mechanical
| Property | Condition | SD390 | SD490 | Difference |
|---|---|---|---|---|
| Yield strength ReH | — | 390–510MPa1 | 490–625MPa1 | +26 % |
| Tensile strength Rm | — | ≥ 560MPa1 | ≥ 620MPa1 | +11 % |
| Elongation after fracture A | test piece similar to No. 2 | ≥ 16%1 | ≥ 12%1 | −25 % |
| Yield-to-tensile ratio Fy/Fu | — | ≤ 0.81 | ≤ 0.81 | same |
Rows are matched by condition (thickness band, temperature, product form). A dash means the grade has no sourced value for that condition. Differences are SD490 relative to SD390; for ranges the lower bound is compared.