Compare / C80/95 vs C60/75
C80/95 vs C60/75
EN 1992-1-1:2004 · Concrete
80 MPa cylinder, 95 MPa cube characteristic strength at 28 days; Ecm 42 GPa.
EN 1992-1-1:2004 · Concrete
60 MPa cylinder, 75 MPa cube characteristic strength at 28 days; Ecm 39 GPa.
Mechanical
| Property | Condition | C80/95 | C60/75 | Difference |
|---|---|---|---|---|
| Secant modulus of elasticity Ecm | 28 days | 42 000MPa2 | 39 000MPa2 | −7.1 % |
| Poisson's ratio ν | uncracked | 0.21 | 0.21 | same |
| Characteristic cylinder strength fck | 28 days | 80MPa3 | 60MPa3 | −25 % |
| Characteristic cube strength fck,cube | 28 days | 95MPa3 | 75MPa3 | −21 % |
| Mean compressive strength fcm | 28 days | 88MPa3 | 68MPa3 | −23 % |
| Mean axial tensile strength fctm | 28 days | 4.8MPa2 | 4.4MPa2 | −8.3 % |
| Characteristic tensile strength (5 % fractile) fctk,0.05 | 28 days | 3.4MPa2 | 3.1MPa2 | −8.8 % |
| Characteristic tensile strength (95 % fractile) fctk,0.95 | 28 days | 6.3MPa2 | 5.7MPa2 | −9.5 % |
| Strain at peak stress εc1 | — | 2.8‰2 | 2.6‰2 | −7.1 % |
| Ultimate strain (analysis curve) εcu1 | — | 2.8‰2 | 3‰2 | +7.1 % |
| Strain at maximum stress (parabola-rectangle) εc2 | — | 2.5‰2 | 2.3‰2 | −8.0 % |
| Ultimate strain (parabola-rectangle) εcu2 | — | 2.6‰2 | 2.9‰2 | +12 % |
| Exponent of the parabola n | — | 1.42 | 1.62 | +14 % |
| Strain at maximum stress (bilinear) εc3 | — | 2.2‰2 | 1.9‰2 | −14 % |
| Ultimate strain (bilinear) εcu3 | — | 2.6‰2 | 2.9‰2 | +12 % |
Design values
| Property | Condition | C80/95 | C60/75 | Difference |
|---|---|---|---|---|
| Long-term coefficient on compressive strength αcc | — | 11 | 11 | same |
| Partial factor for the material γc | persistent and transient design situations | 1.51 | 1.51 | same |
Physical
| Property | Condition | C80/95 | C60/75 | Difference |
|---|---|---|---|---|
| Unit weight γ | reinforced, normal percentage of reinforcement | 25kN/m³1 | 25kN/m³1 | same |
Thermal
| Property | Condition | C80/95 | C60/75 | Difference |
|---|---|---|---|---|
| Coefficient of thermal expansion α | — | 10×10⁻⁶ /K1 | 10×10⁻⁶ /K1 | same |
Rows are matched by condition (thickness band, temperature, product form). A dash means the grade has no sourced value for that condition. Differences are C60/75 relative to C80/95; for ranges the lower bound is compared.