Compare / A1085 vs S355J2H (EN 10210, hot finished)
A1085 vs S355J2H (EN 10210, hot finished)
ASTM A1085/A1085M · Steel
US HSS with a yield cap: 50–70 ksi (345–483 MPa), 65 ksi (450 MPa) tensile, same for round and shaped.
EN 10210 · Steel
Hot finished hollow sections: 355 MPa yield up to 16 mm, 470–630 MPa tensile — and fu = 490 MPa in design, not the 510 MPa of cold-formed EN 10219 sections.
Mechanical
| Property | Condition | A1085 | S355J2H (EN 10210, hot finished) | Difference |
|---|---|---|---|---|
| Yield strength ReH | t = 16 mm | 345–483MPa1 | ≥ 355MPa1 | +2.9 % |
| t = 40 mm | 345–483MPa1 | ≥ 345MPa1 | same | |
| Tensile strength Rm | t = 100 mm | ≥ 450MPa1 | 470–630MPa1 | +4.4 % |
| Elongation after fracture A | — | ≥ 21%1 | ≥ 22%1 | +4.8 % |
Rows are matched by condition (thickness band, temperature, product form). A dash means the grade has no sourced value for that condition. Differences are S355J2H (EN 10210, hot finished) relative to A1085; for ranges the lower bound is compared.