Compare / S355J2H (EN 10210, hot finished) vs A500 Grade C
S355J2H (EN 10210, hot finished) vs A500 Grade C
EN 10210 · Steel
Hot finished hollow sections: 355 MPa yield up to 16 mm, 470–630 MPa tensile — and fu = 490 MPa in design, not the 510 MPa of cold-formed EN 10219 sections.
ASTM A500/A500M · Steel
The usual US HSS grade: 50 ksi (345 MPa) yield shaped, 46 ksi (315 MPa) round, 62 ksi (425 MPa) tensile.
Mechanical
| Property | Condition | S355J2H (EN 10210, hot finished) | A500 Grade C | Difference |
|---|---|---|---|---|
| Tensile strength Rm | t = 100 mm | 470–630MPa1 | ≥ 425MPa2 | −9.6 % |
Rows are matched by condition (thickness band, temperature, product form). A dash means the grade has no sourced value for that condition. Differences are A500 Grade C relative to S355J2H (EN 10210, hot finished); for ranges the lower bound is compared.